Synthesis and Characterization of Vinyltrimethoxylsilane/Acrylated Epoxy Resin Dipolymer

徐劲祥; 吴小军

您当前的位置：

首页 >

文章列表页 >

Synthesis and Characterization of Vinyltrimethoxylsilane/Acrylated Epoxy Resin Dipolymer

更新时间：2026-09-14

- Synthesis and Characterization of Vinyltrimethoxylsilane/Acrylated Epoxy Resin Dipolymer
- AE/VTMS二元共聚物的合成研究
- Issue 3, Pages: 231-235(2007)
- 作者机构：
  
  1. 北京理工大学宇航科学技术学院
  2. 中北大学机电工程学院
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：2007
- 稿件说明：
移动端阅览
徐劲祥, 吴小军. Synthesis and Characterization of Vinyltrimethoxylsilane/Acrylated Epoxy Resin Dipolymer[J]. 2007, (3): 231-235.
DOI：

徐劲祥, 吴小军. Synthesis and Characterization of Vinyltrimethoxylsilane/Acrylated Epoxy Resin Dipolymer[J]. 2007, (3): 231-235. DOI：

摘要

以丙烯酸环氧树脂(AE)

乙烯基三甲氧基硅烷(VTM S)为单体

通过溶液聚合制备了含有机硅氧烷的二元共聚物溶液.通过正交实验对工艺条件进行了优化

研究了单体配比对转化率的影响

并用IR表征了共聚物的结构

热失重法(TGA)对其稳定性进行了分析测试.结果表明:共聚物中成功地引入了有机硅链节

且随着硅含量的增加

共聚物耐热性提高.

Abstract

The dipolymer using vinyltrimethoxysilane and acrylated epoxy resin as monomer was synthesized by means of solution copolymerization.Technological process of reaction was optimized by the cross experiment.At the same time

the structure of dipolymer were examined by using of the apparatus-IR. The thermal stabilities of polyurethane were examined by TGA.The results showed that silicone chains were successfully introduced into the dipolymer.With the increasing of amount of silicon

heat-resistant of polymer will be increased.

关键词

Keywords

references

陈丽琼,刘杰,李纬,等.乙烯基硅烷-丙烯酸酯乳液共聚动力学研究[J].功能高分子学报,2003,16(2):166-170.Cheng Liqing,Liu Jie,Li Wei,et al.A kinetic study of emulsion copolymerization of vinyl silane-acrylates[J].Journalof Functional Polymers,2003,16(2):166-170.(in Chinese)

Smith S D,DeSimone J M,Huang H,et al.Synthesis and characterization of poly(methyl methacrylate)-g-poly(dimethylsiloxane)copolymers[J].Macromolecules,1992,25(10):2575-2581.

Helary G,Migonney V,Belleney J,et al.Terpolymerization of 3-methacryloxypropyl Tri(trimeth-ylsiloxy)silane,methacrylate acid and dimethyl octyl ammonium styrene sulfonate:determination of the reactivity rations[J].EuropeanPolymer Journal,2000,36(11):2365-2369.

Park H S,Yang I M,Wu J P,et al.Synthesis of silicone-acrylic resins and their applications to super weatherablecoatings[J].Journal of Applied Polymer Science,2001,81:1614-1623.

Fawcett A H,Foster A B,Hania M,et al.Silicone graft copolymers with styrene,methylmethacrylate and chloroprene[J].Polymer Preprints,2001,42(1):213-214.

刘胜峰,王华林,秦广龙,等.丙烯酸树脂与聚硅氧烷接枝改性的研究[J].涂料工业,1996(2):6-8.Liu Shengfeng,Wang Hualin,Qin Guanglong,et al.Study on acrylic resin and its grafting modification withpolysiloxane[J].Paint&Coatings Industry,1996(2):6-8.(in Chinese)

余锡宾,王华林.丙烯酸树脂与聚硅氧烷接枝改性的研究[J].高分子材料科学与工程,1998,14(2):129-131.Yu Xibing,Wang Hualing.Research on graft modification of acrylic resin and polyalkoxysilane[J].Polymeric MatericScience&Cngineering,1998,14(2):129-131.(in Chinese)

黄光速,何其佳,江璐霞.聚苯基烷氧基/聚丙烯酸酯同步互贯网络聚合物阻材料的研究[J].高分子材料科学与工程,2001,17(2):133-136.Huang Guangsu,He Qijia,Jiang Luxia.Study on damping materials of polyphenylsiloxane/polyacrylate sin[J].Polymeric Materic Science&Cngineering,2001,17(2):133-136.(in Chinese)

王燕,张宝力,朱柯,等.丙烯酸有机硅共聚物乳液聚合及性能研究[J].涂料工业,2000(10):67-69.Wang Yan,Zhang Baoli,Zhu Ke,et al.Properties study of emulsion copolymerization of silane-acrylates[J].Paint&Coatings Industry,2000(10):67-69.(in Chinese)

Views

107

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Study on Synthesis of Heat-Resistance Polyurethane

Study on the Removal of CO2 in Confined Space by High⁃Gravity Enhanced Potassium Hydroxide Coupled Potassium Glycinate Solution

Design of Parallel Robot Experimental Platform Based on Reconfigurable Innovative Components

High⁃Precision Photoeletric Coordinate Positioning Technology Based on Transformer⁃FPGA Collaborative Feature Modeling

Configuration Design and Research of a Hybrid Quadruped Perilla Sowing Robot

Related Author

吴晓青

崔璐娟

左海丽

卫晓利

Related Institution

中北大学理学院

⁰