紫外光固化胶粘剂的制备及性能研究

张丽华; 陈军

您当前的位置：

首页 >

文章列表页 >

紫外光固化胶粘剂的制备及性能研究

更新时间：2026-09-14

- 紫外光固化胶粘剂的制备及性能研究
- 紫外光固化胶粘剂的制备及性能研究
- Issue 2, (2003)
- 作者机构：
  
  1. ,山西,太原,030051
  2. 华北工学院化学工程系
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：2003
- 稿件说明：
移动端阅览
张丽华, 陈军. 紫外光固化胶粘剂的制备及性能研究[J]. 2003, (2).
DOI：

张丽华, 陈军. 紫外光固化胶粘剂的制备及性能研究[J]. 2003, (2). DOI：

摘要

　研究了一种紫外光固化胶粘剂的制备及性能.以甲苯二异氰酸酯和甲基丙烯酸羟乙酯为基本原料合成预聚物

再添加光引发剂、活性稀释剂等

制成紫外光固化胶粘剂;采用该胶粘剂粘接试片

考察了贮存时间对光固化时间和粘接强度的影响.通过正交试验获得了紫外光固化胶粘剂的较佳配比和制备条件.所研制的光固化胶粘剂在制出之后放置约20h

其性能将较为稳定.

Abstract

To research the preparation of an ultravioletcuring adhesive and its behavior

prepolymer was synthesized when tolylene diisocyanate and 2hydroxyethyl methacrylate were used as basic raw materials. Ultravioletcuring adhesive was prepared through adding photoinitiator and active diluent etc. into the prepolymer. By means of bonding testpieces with this adhesive

the effect of shelftime on curing time and adhesion strength has been investigated. The better formulation and preparation conditions of ultravioletcuring adhesives were obtained through orthogonal experiment. The properties of concerned ultravioletcuring adhesives will be more stable after 20 h when prepared.

关键词

Keywords

references

Views

661

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Hopkinson Bar Pulse Width Extension Test Method Based on Polyurethane Wave Shaper

高g值冲击下聚氨酯缓冲仿真研究

Research on the Optimal Combination of Tail⁃Beat Frequency and Swing of Fish During Self⁃Propelled Swimming

Network Intrusion Detection Model Based on Recurrence Plot and MobileViT⁃AESTF

Research Progress on Single⁃Photon Detection for Quantum Information About Mechanisms，Devices and Circuit Design

Related Author

Guo Tao

Chen Liang

Li Xiangyu

Zhao Rui

Shi Yunbo

Chen Yunan

Zhang Peng

石亦琨

Related Institution

Key Laboratory of Electronic Testing Technology， North China University of Technology

Shanxi Institute of Mechanical and Electrical Engineering

中北大学电子测试技术重点实验室

北京星途探索科技有限公司

⁰