采用掺加聚丙烯纤维和聚合物乳液对水泥砂浆进行改性.运用正交实验直观分析的方法

确定了聚丙烯纤维聚合物乳液改性水泥砂浆材料成分的最佳配比

并且对改性水泥砂浆进行了力学性能研究.实验结果表明

掺加一定量的聚丙烯纤维和聚合物乳液

可以提高水泥砂浆的力学性能

并且得出其作用机理.

Abstract

Polypropylene fibers and polymer emulsion were filled into cement mortar to enhance its behavior.An orthogonal investigation was conducted on polypropylene fiber and polymer emulsion reinforced cement mortar

the optimum ratio was determined and its mechanical properties were studied.The test results showed that the mechanical properties of cement mortar could improve by filling some polypropylene fiber and polymer emulsion together into it.The mechanism of the above enhancement of mechanical properties was analyzed.

关键词

Keywords

references

Views

204

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

聚丙烯纤维/聚合物乳液对砂浆干缩开裂的影响

Effect of Solution Aging Treatment on the Microstructure and Properties of TC4 Titanium Alloy

Study on Performance of Fly Ash-Metakaolin Base Geopolymer Concrete

二胺/TDI体系聚氨酯弹性体耐热性能的研究

碳纳米管/高密度聚乙烯复合薄膜的结构与性能研究

Related Author

王英姿

DONG Ruifeng

ZHAO Yuhong

GUO Yumo

LI Jiaxiang

YAN Xiaokun

LI Yamin

SUN Xueliang

Related Institution

School of Materials Science and Engineering， North University of China

MOE Jointly Collaborative Innovation Center for High-Performance Al/Mg Based Materials， North University of China

Shanxi Key Laboratory of Intelligent Casting and Advanced Forming for New Materials， North University of China

Beijing Advanced Innovation Center for Materials Genome Engineering， University of Science and Technology Beijing

Shanxi Provincial Technology Innovation Center of Collaborative Disposal and Low-Carbon Utilization of Industrial Solid Waste

⁰