The fabrication

characterization and properties of holl ow titania(TiO2)spheres was presented through a solvothermal process with C micro-spheres template synthetic route using glucose

TBOT

and HCl as raw mat erials.The XRD

SEM and TEM results show that as-prepared products of hollow Ti O2 spheres are anatase

and they are uniform spherical within a narrow si ze distribution

and are typically hollow structured

respectively.The products are studied through UV-vis and BET

and the results show that the light adsorp tion edge of products moves a remarkable red shift to 750 nm

and the mesoporous products have a high surface area

pore volume and average pore size of 99.8 m 2·g-1

0.62 cm3·g-1

and 5.3 nm

respectively.